Morgan Introduces New TCA 125 Brick for Aluminium Smelting

16/03/2015

Anodes, which are crucial to the transformation of alumina into aluminium, are generally fired in graphite, in anode baking furnaces that incorporate insulation bricks. However, historically these bricks have been subject to damage and compromise as a result of the baking process, and a better quality alternative has long been sought.

With the TCA 125 brick, Morgan is providing that alternative. The TCA 125 has a cold crush strength of at least 8.0 MPa and permanent linear change (PLC) below 1% at 1350°C after 12 hours of firing. Previously, bricks of this quality had to be produced on hydraulic presses, however, extended development and experimentation by Morgan's development team in Casalpusterlengo, Italy, has resulted in the formulation of a new composition that allows such bricks to be produced using the ‘Slinger’ process, yet still achieve all of the properties required, in compliance with ASTM norms.

The ‘Slinger’ process is a form of low-pressure extrusion of a wet clay mix containing high levels of burnout additives, with the additional processing step that the semi-extruded material gets ‘slung’ onto a continuous belt to generate additional porosity, before drying and firing.

Massimiliano Marchetti of Morgan Advanced Materials explained that the TCA 125 bricks are part of a new product initiative, adding: “A number of products, in particular monolithics, have already been launched onto the market and other new brick types are also set to be released this year".

Morgan can now produce TCA 125 bricks in various sizes up to a maximum 640×250×76 mm (25 x 10 x 3 inch), including the standard 3-inch (76mm), Italian, German and French brick sizes. The company can also supply a wide range of high temperature insulation bricks and monolithics, as well as fire protection materials suitable for many applications and industries.

For more information, please visit www.morganthermalceramics.com/IFB-TC125

Morgan Thermal Ceramics,
Morgan Advanced Materials,